The choice of sculptural liquid silicone and curing agent

When you copy a garden sculpture model, we often use copying silicone mold and curing agent according to a certain ratio to complete the operation, of which the technical parameters to select(hardness, viscosity, shrinkage, etc.)and copy silicone mold and the radio of curing agent case we have to choose the most suitable one to produce good sculpture models. Copying Silicone mold mainly used for toy and gift industry, craft gift industry, furniture decoration industry, figures copied, building decoration industry, resin handicraft industry, unsaturated resin crafts industry, the plastic toy industry and candle crafts industry, gifts industry, stationery industry, gypsum gifts industry, mold manufacturing industry, bolero craft, simulation plant and animal sculptures industry, Buddhist carvings crafts products and other industries copy and mold making. ①Copying silicone mold has a better operating properties. ②Copying silicone mold has better fluidity, low viscosity and is easy to opera
Post a Comment
Read more
Recent posts

Adult sex products liquid silicone use FAQs

Adult sex products for the two-component addition cure silicone rubber, consists of two parts: A component is a silicone, B component is a curing agent; two components mix ratio of 1:1 ratio. After vulcanization becomes soft, resilient material of low hardness after curing, good tear resistance, good color sense, good texture and other characteristics. Can be made, such as the human body, insoles, shoulder pads, patch, anti-slip mats and other flexible silicone rubber products, but also for the simulation of human facial silicone molds, mainly for the human face, supplies, human organs, mimicking the body shape, the same type, changing shape, soft touch. Adult supplies silicone had a very strong smell, which is due to not using odorless curing agent in the production of secondary sulfur can remove this odor, the harm to the human body is very small and can be ignored, and this is inevitable scented products after all any vulcanized silicone products will smell over time. Friendly remin
Post a Comment
Read more

About artificial culture stone-colored silicone molds difficult problem

Currently the production of artificial culture stone steps mainly in ten steps, namely: model sculpture model processing → Templates → production → Templates → Partition → model paste brushing silicone mold release preparations →  first layer of silicone brush silicone perfusion → off mode. According to the above ten steps, we can see that the production of artificial culture stone mold is the most important use of templates. Artificial culture stone silicone Culture stone generally use a silicone mold, the first use of ocher color modulation, culture stone, culture brick color palette depending on the circumstances, the color of soil is basically a dozen colors, different colors can be mixed to achieve the color you need, color is a key issue, the color is not uniform culture stone, generally do so, first bring up the light brown, and then bring up the gray, light gray in the recall, these three different colors sprayed internal mold, not the whole entire spray again, put the mold int
Post a Comment
Read more

Clear electronic silicone potting compounds

Two-component RTV silicone rubber compounds cure by adding a specified amount of a curing agent to the base compound. Like one-component RTV silicone rubbers, two-component RTV silicone rubbers have outstanding electrical properties and resistance to heat and cold, while also offering improved deep-section curability and storage stability. Features: 1. Properties identical to those of one-component RTV silicone rubber. 2. Electrical properties, heat and cold resistance, shock resistance, weather resistance, curing characteristics, etc. 3. Deep-section curability. 4. The curing reaction proceeds uniformly at the surface and internally, regardless of rubber thickness. 5. The adjustability of cure speed. 6. Cure time can be adjusted by changing the type or quantity of curing agent, or by heating. Storability The base compound and curing agent are stored separately, so the product will not become unusable due to curing during storage. Two-component RTV silicone rubbers can be stored for lo
Post a Comment
Read more

FAQs about the use of rtv liquid silicone rubber

1. Why silicone mold will be fewer turning models ? If the products do little more complex patterns come with a large hardness silicone mold, there will be a fewer turning molded phenomenon, because silicone excellent time will be very brittle and easily broken. Conversely, if you do build a product to do with a small hardness silicone mold, the result will also be unsatisfactory. Because silicone is too soft, it will reduce the tensile and tear strength, made out of the mold will be deformed, turning model number will be reduced. Mold itself good quality, silicone no good or bad, only suitable or unsuitable. We want to use for the product to make the hardness of the size of the silicone mold will not appear in this situation. 2. Why mold silicone mold phenomenon appears to burn ? Because unsaturated resin and resin products plus a peroxide curing agent after the case of the resin reaction will generate a lot of heat, usually resin curing time is 3 minutes, then three minutes after goi
Post a Comment
Read more

The proportions and reactions of the curing agent and the liquid silicone

  The amount of the curing agent depends on the actual requirements of customers. If molds require fast drying and demould, more curing agent is needed, and the mixing ratio shouldn’t be over 5％, the more curing agent, the faster the molding time. Or it will waste the silicone rubber. Contrarily, it is the silicone potting mold, less curing agent will be needed to lengthen the operation time. The mixing ratio of silicone and the catalyst shouldn’t below 1％, otherwise, it would need a longer curing time. With the mixing ratio less than 5%, it would have little influence on the hardness, tear strength, and tensile strength. Silicone and the catalyst: 1. Curing agent 1% added, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours. 2. Curing agent 2% added, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours. 3. Curing agent 3% added, the silicone can still be operated within 28 - 30 minutes and can be demou
Post a Comment
Read more

rtv-2 liquid silicone rubber not curing the reason

Users sometimes use liquid silicone curing problems encountered, now our summarizes five kinds of the cause of the rtv-2 liquid silicone not curing and their solutions, we hope to help. 1. A curing agent or too little of the curing agent will affect the cured silicone. According to the provisions of the curing agent is added, and should see clear instruction is the proportions of the volume or weight. 2. Different types of curing agents can’t mix, add molding glue exposure to tin ingredients in the condensation silicone will not respond. With the corresponding models of the curing agent. Operating tools are classified, do not mix. If you are operating plus molding silicone, do not come into contact with condensation products. 3. Silicone and curing agent do not stir evenly. Silicone and curing agent operation to fully stir well. 4. Incomplete cure (not dry) in the contact surface occurs only master, the other parts of the intact curing. Marked on the surface of the master mold with a t
Post a Comment
Read more